PPR Pipe Granules PA14D Polypropylene, Random Copolymer MI 0.26

Product Description:

PA14D is a high-performance polypropylene raw material.

It has excellent heat resistance and creep resistance.

PPR Pipe Granules made of PA14D ensure stable performance.

It can withstand temperatures from -20℃ to 110℃.

Low thermal conductivity reduces heat loss effectively.

PA14D features smooth surface and easy processing.

It has strong impact resistance and no easy cracking.

Non-toxic and odorless, compliant with drinking water standards.

Good chemical inertness, resistant to corrosion and scaling.

Lightweight design facilitates transportation and installation.

PA14D PPR Pipe Granules have long service life.

Ideal for producing hot and cold water supply pipes.

Suitable for residential, commercial and industrial use.

It ensures seamless hot-melt connection without leakage.

Stable batch performance, easy to form uniform pipes.

Resistant to aging, adapting to various environments.

It meets international quality and safety certifications.

PA14D enhances pipe rigidity and pressure resistance.

Suitable for new construction and renovation projects.

Low maintenance cost, saving time and money for users.

Environmentally friendly and recyclable, green and eco-friendly.

It provides reliable raw materials for water pipe manufacturing.

Balances high performance and cost-effectiveness perfectly.

The product has passed the RoHS,FDA,GB17219-1998 Safety Evaluation Standards forDrinking Water Transportation and Distribution Equipment and Protective Materials, GB/T18252-2008Long temm Hydrostatic Strength Test, and GB/T6111-2003 Thermal Stability Test under HydrostaticConditions. Widely used in cold and hot water supply pipes, plates, storage tanks, modified products, etc.

Basic Information

Origin: shandong, China

Model Number: Jingbo PA14D

MFR: 0.26 (2.16kg/230°)

Packaging Details: Heavy-duty packaging film bags, net weight 25kg per bag.

Port: Qingdao

Payment: t/t. LC at sight

Customs Code: 39021000

The amount of time from order placement to dispatch:

Quantity(tons)	1-200	>200
Lead time (days)	7	To be negotiated

Technical performance index parameters（TDS)

ITEM	UNIT	METHOD	TYPICAL VALUE
Melt Flow Rate (MFR)	g/ 10min	GB/T 3682	0.26
Ash Content	%	GB/T 9345.1	0.011
Yellowness Index	/	HG/T 3862	-2.1
Tensile Stress @ Yield	MPa	GB/T 1040	24.5
Tensile modulus of elasticity	MPa	GB/T 1040	786
Tensile Stress @ break	MPa	GB/T 1040	26.5
Tensile Stress Nominal Strain	%	GB/T 1040	485
Flexural Modulus	MPa	GB/T 9341	804
Charpy Impact Strength（23℃)	kJ/m2	GB/T 1043	56
Charpy Impact Strength（-20℃)	kJ/m2	GB/T 1043	2.7
DTUL	℃	GB/T 1634.2	76
Rockwell Hardness（ R）	/	GB/T 3398.2	83
Moulding Shrinkage（ SMp)	%	GB/T 17037.4	1.2
Moulding Shrinkage (SMn)	%	GB/T 17037.4	1.2
Melting Temperature	℃	GB/T 19466.3	145
Oxidation induction time (210 ℃, aluminum dish)	min	GB/T 19466.6	44.5
Fixed Bending Stress	MPa	GB/T 9341	19.2